Synthesis of Hyper-branched Polymer with Terminal Amidogen and its Application as Formaldehyde Scavenger in Leather

Abstract

A hyperbranched polymer with terminal amidogen was synthesized with succinic anhydride and diethylenetriamine by “one-step method”, and then it was characterized through FT-IR and GPC testing. Moreover, the prepared hyperbranched polymer with terminal amidogen was used to remove free formaldehyde in leather tanned by organic phosphonium tanning agent. The application results indicated that the formaldehyde-removal percentage of hyperbranched polymer with terminal amidogen reached 60.4%. The formaldehyde content of leather reduced to less 50mg/kg. Comparing with other formaldehyde scavengers, its formaldehyde-removal effect was much better. The thickening rate and dye absorptivity of the polymer were 16.7% and 96.5% respectively, so it also had thickening and assisting dyeing effects to leather.ResumenUn polímero hiper-ramificado con terminal amidógeno fue sintetizado con anhídrido succínico y dietilentriamina por "un método de un paso" y, a continuación, se caracterizó mediante pruebas de FT-IR y GPC. Por otra parte, el polímero hiper-ramificado preparado con terminal amidógeno fue utilizado para eliminar el formaldehído libre en el cuero curtido con fosfonio orgánico como agente curtiente. Los resultados indicaron que el porcentaje de remoción del formaldehído del polímero hiper-ramificado con terminal amidógeno alcanzó 60,4%. El contenido de formaldehído en el cuero fue reducido a menos 50mg/kg. Comparando con otros removedores de formaldehído, el efecto de eliminación del formaldehído fue mucho mejor. El grado de engrosamiento y la absorción de la tintura del polímero fueron 16,7% y 96,5% respectivamente, por lo que también hubo aumento de espesor y un efecto de asistencia al teñido en el cuero.