Utilization of Chromium-tanned Leather Solid Wastes in Microencapsulation

Abstract

In this research, solid collagen-based protein hydrolysate was isolated from chromium-tanned leather wastes and its chemical properties were determined. After that, the use of collagen hydrolysate (CH) was investigated as a polymeric wall material in the microencapsulation process. The effects of variations in concentrations of CH, lavender oil (LO) and glutaraldehyde (GA), which were used during the microencapsulation process, on the oil load of microcapsules, oil content, encapsulation efficiency and release rate of oil were determined. The morphological structure of the microcapsules was investigated using optical and scanning electron microscopes (SEM). It was determined by FTIR studies that there was no evidence for any significant interaction between CH and LO.RESUMENEn esta investigación, un hidrolizado colágenico sólido se aisló de desechos de cuero al cromo y sus propiedades químicas fueron determinadas. Luego, el uso del hidrolizado colágenico (CH) fue investigado como un material polimérico para utilizarse como componente estructural en los procesos de micro-encapsulación. Los efectos atribuibles a la variaciones en concentraciones de CH, aceite [esencial] de Lavanda (LO) y glutaraldehído (GA) que se utilizaron en el proceso de micro-encapsulación, sobre la carga aceitosa presente en las micro-cápsulas, el contenido de aceite, la eficiencia en encapsulación, y la velocidad de descarga del aceite fueron determinadas. La estructura morfológica de las micro-cápsulas se investigó por medio de microscopia electrónica por barrido (SEM). Se determinó también por medio de estudios FTIR que no hubo apreciable evidencia de interacción entre CH y LO.