Effects of Atmospheric Pressure Plasma Treatments on Various Properties of Leathers

Abstract

Chrome tanned crust leathers were treated with atmospheric pressure plasma with argon flows at different times. The leather was then dyed with acid and metal complex dyes. The dyestuff concentration in the exhausted dye bath, CIE lab color analysis, hydrophilicity, FTIR spectra and SEM images were compared for 0, 2.1, 4.2 and 6.4 sec/cm2 durations of plasma. In addition, various physical properties such as rubbing fastness, tear loading and tensile strength were also examined to see the effects of increased duration of the plasma process. The presence of ions that appeared during this process in an atmospheric environment was determined by OES. The best results were obtained from leather subjected to 6.4 sec/cm2 of argon gas atmospheric pressure plasma.ResumenCrosta de cueros al cromo fueron tratados por medio de plasma a presión atmosférica en flujos con Argón durante diferentes tiempos. El cuero luego fue teñido con colorantes aniónicos así como también complejos metálicos. La concentración del colorante en los baños agotados, CIE lab color analysis de Hunter Laboratories, Hidrofilicidad, Espectroscopia IR. Fourrier, e imágenes electro microscópicas por barrido electrónico, fueron comparadas a 0, 2.1, 4.2 y 6.4 seg/cm² de tiempos de aplicación del plasma. En adición ciertas propiedades físicas como resistencia al frote, carga al momento de rotura, resistencia a la rotura, fueron examinadas para determinar los efectos del tiempo cuando el cuero fue sometido a la acción del plasma. La presencia de iones resultantes del Argón a presión atmosférica fueron determinados por OES. Los mejores resultados fueron obtenidos en cuero sometido 6,4 seg/cm² tiempo de contacto con el plasma de argón a presión atmosférica.